Multiaxial include Uni-Directional,Biaxial,Triaxial and Quadraxial Fabrics.The entire Partial warp.weft and double bias plies are stitched into a single fabric.Withou filament crimp in woven roving,the Multiaxial fabrics are in advantage of high strength,excellent stiffness,low weight and thickness,as well as the improved fabric surface quality. The fabrics can be combined with chopped strand mat or tissue or nonwoven materials.
Uni-Directional Fabric( 0°or 90°)
The density of 0° Uni-Directional Fabric can be 300g/m²~900g/m² and density of 90° can be 150g/m²~1200g/m²
Biaxial Fabric（0°/90°or ±45°）
The density can be 300g/m²~2400g/m² ,can be wich layer of Chopped Strands.
Triaxial Fabric（0°/+45°/-45°）/ (+45°/+90°/-45°)
The density can be 450g/m²~1800g/m² ,can be wich layer of Chopped Strands.
The density can be 600g/m²~2000g/m² ,can be wich layer of Chopped Strands.
1.Mechanical property of different directions is adjustable.
2.The multi-layers structure could simplify forming process, improve operation efficiency.
3.Quickly wet-out, good molding property, easily to delete air bubbles.
It is compatible with UP,Viny Ester and Epoxy etc,used in GRP pultrusion process,hand lay-up process and RTM process etc,out-made products include GRP boats,automobile parts,wind enegry blades etc.
E-Glass Multiaxial fibreglass fabricis wound onto a paper tube which has an
inside diameter of 90mm. The roll outside diameter is approximately 265mm.
Each roll is wrapped up in plastic film and then packed in a cardboard box. The
rolls are stacked horizontally or vertically onto pallets. All pallets are stretch
wrapped and strapped to maintain stability during transport.
This product should be stocked in dry and cool places. The best condition is with temperature between 15-35 °c, with a relative humidity between 30% and 70%. Please keep the product in its original packing before use to avoid moisture.